Integrated LaB6/g-C3N4 solar absorber for solving dye accumulation during solar steam generation

Solar steam generation has attracted considerable interest due to its easy accessibility and sustainability. However, dye molecules were gradually concentrated on bulk water or the surface of solar absorbers during the disposal of dye wastewater. Herein, LaB₆/g-C₃N₄ composites were immobilized on porous cotton cloth, served as a solar absorber resistant to dye clogging. The optimal solar absorber possessed solar harvesting of 92.3% and showed great application potential in the field of the treatment of dye wastewater. This study presented a new approach for the treatment of dye wastewater.     

Synthesis,structure, CO oxidation,and H2 production activities of CaCu3−xMnxTi4−xMnxO12 (x = 0, 0.5, and 1.0)

Synthesis of nanocrystalline pristine and Mn-doped calcium copper titanate quadruple perovskites, CaCu_3?xMn_xTi_4?xMn_xO₁₂ (x = 0, 0.5, and 1.0) by modified citrate solution combustion method has been reported. Powder X-ray diffraction patterns attest the phase purity of the perovskite materials. Average particle sizes of all the materials obtained from the Scherrer's formula are in the range of 55–70 nm. The specific surface areas for all the perovskites obtained from BET isotherms are found to be low as expected for the condensed oxide systems and fall in the range of 13–17 m² g^?1. Transmission electron microscopy studies show a reduction in particle size of CaCu₃Ti₄O₁₂ with increase in Mn doping. Ca and Ti are present in +2 and +4 oxidation states in all the materials as demonstrated by X-ray photoelectron spectroscopy analyses. Cu²⁺ gets reduced in CaCu₃Ti₄O₁₂ with higher Mn content. Mn is observed to be present only in +3 oxidation state. All the materials have been examined to be active in CO oxidation as well as H₂ production from methanol steam reforming. CaCu₃Ti₄O₁₂ with ~14 at.% Mn is found to show best catalytic activities among these materials. A comprehensive analysis of the catalytic activities of these perovskites toward CO oxidation and H₂ production from MSR reveal the cooperative activity of copper-manganese in the doped perovskites and it is more effective at lower manganese content.     

电网设备线夹开裂原因

某电力公司变电站用铝合金设备线夹在运行过程发生批次开裂事故,通过宏观观察、断口分析、化学成分分析、力学性能测试、冷冻模拟试验等方法,对设备线夹的开裂原因和开裂机理进行了分析。结果表明:设备线夹焊缝存在焊接缺陷,导致焊缝强度下降;设备线夹接线管底部存在积水空间,寒冷天气下积水结冰,体积膨胀,使焊缝承受设计工况外的负载而过载开裂,造成了线夹开裂。     

Water vapor volatilization and oxidation induced surface cracking of environmental barrier coating systems: A numerical approach

A numerical model is developed for surface crack propagation in brittle ceramic coatings, aiming at the intrinsic failure of rare-earth silicate environmental barrier coating systems (EBCs) under combustion conditions in advanced gas turbines. The main features of progressive degradation of EBCs in such conditions are captured, including selective silica vaporization in the top coat due to exposure to water vapor, diffusion path-dependent bond coat oxidation, as well as crack propagation during cyclic thermal loading. In light of these features, user-defined subroutines are implemented in finite element analysis, where surface crack growth is simulated by node separation. Numerical results are validated by existing experimental data, in terms of monosilicate layer thickening, thermal oxide growth, and fracture behaviors. The experimentally observed quasi-linear oxidation in the early stage is also elucidated. Furthermore, it is suggested that surface crack undergoes rapid propagation in the late stage of extended thermal cycling in water vapor and leads to catastrophic failure, driven by both thermal mismatch and oxide growth stresses. The latter is identified as the dominant mechanism of penetration. Based on detailed analyses of failure mechanisms, the optimization strategy of EBCs composition is proposed, balancing the trade-off between mechanical compliance and erosion resistance.     

Simulation of thermal barrier coating spallation induced by the initiation/growth/coalescence of internal crack and interfacial crack based on a real image model

In the furnace cycle test, the growth of oxide film leads to the propagation and coalescence of multiple cracks near the interface, which should be responsible for the spallation of thermal barrier coatings (TBCs). A TBC model with real interface morphology is created, and the near-interface large pore is retained. The purpose of this work is to clarify the mechanism of TBC spallation caused by successive initiation, propagation, and linkage of cracks near the interface during thermal cycle. The dynamic growth of thermally grown oxide (TGO) is carried out by applying a stress-free strain. The crack nucleation and arbitrary path propagation in YSZ and TGO are simulated by the extended finite element method (XFEM). The debonding along the YSZ/TGO/BC interface is evaluated using a surface-based cohesive behavior. The large-scale pore in YSZ near the interface can initiate a new crack. The ceramic crack can propagate to the YSZ/TGO interface, which will accelerate the interfacial damage and debonding. For the TGO/BC interface, the normal compressive stress and small shear stress at the valley hinder the further crack propagation. The growth of YSZ crack and the formation of through-TGO crack are the main causes of TBC delamination. The accelerated BC oxidation increases the lateral growth strain of TGO, which will promote crack propagation and coalescence. The optimization design proposed in this work can provide another option for developing TBC with high durability.     

海上稠油油田蒸汽吞吐产量确定新方法

针对目前蒸汽吞吐产量预测模型假设条件简单、普适性差等问题,一般采用测试法和类比法综合确定海上稠油油田蒸汽吞吐初期产量。由于目前海上油田通常只开展常规测试,无法直接获得热采开发初期产量。笔者提出海上稠油油田蒸汽吞吐初期产量确定新方法,建立蒸汽吞吐相对于常规开发的初期产量倍数预测模型,通过蒸汽吞吐产量倍数,将常规测试确定的产量转化为蒸汽吞吐产量。研究表明,蒸汽吞吐初期产量倍数主要受储集层渗透率、原油黏度、注入强度、蒸汽干度等因素影响,利用正交试验设计和多元回归等方法,建立海上稠油油田蒸汽吞吐初期产量倍数与油藏地质参数及注入参数之间的非线性预测模型,该模型经实际生产数据验证,预测误差小于5%,可靠性高,能够为海上稠油油田蒸汽吞吐初期产量的确定提供依据。     

浅析火力发电厂汽水系统中内径管与外径管的设计选择

按照管道加工工艺的不同,管道可分为内径控制管和外径控制管。通过热轧工艺生产的外径控制无缝钢管,可满足火力发电厂汽水系统中绝大部分管道的使用要求。对于超(超)临界机组的主蒸汽和高温再热蒸汽管道采用的P91/P92材质的大口径厚壁无缝钢管,由于对材料性能和加工工艺有特殊要求,因此宜采用内径控制管。     

Inhibition of stress corrosion cracking in 304 stainless steel through titanium ion implantation

The effects of titanium ion implantation on the stress corrosion cracking (SCC) behaviour of 304 austenitic stainless steel were studied. Slow strain rate tests (SSRTs) were conducted on 304 steel in air and in 5?wt-% NaCl solution. The microscopic effects of ion implantation were evaluated by Stopping and Range of Ions in Matter Procedures (SRIM). Fracture morphologies and microstructures were investigated by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The fracture surfaces illustrate that ion implantation significantly inhibits the corrosion pits that initiate SCC. A dense passive film, which inhibits SCC, was formed during the ion implantation process. SCC initiation was restrained due to the dense dislocation nets that were generated by titanium ion implantation.

Highlights

• Ion implantation inhibits SCC susceptibility.

• The lack of Cr at the grain boundary leads to the expansion of SCC along the grain boundary.

• Implantation-induced damage leads to high-density dislocations.

• The surface was amorphised due to high-density dislocations.

     

Catalytic steam reforming of tar for enhancing hydrogen production from biomass gasification: a review

Presently, the global search for alternative renewable energy sources is rising due to the depletion of fossil fuel and rising greenhouse gas (GHG) emissions. Among alternatives, hydrogen (H₂) produced from biomass gasification is considered a green energy sector, due to its environmentally friendly, sustainable, and renewable characteristics. However, tar formation along with syngas is a severe impediment to biomass conversion efficiency, which results in process-related problems. Typically, tar consists of various hydrocarbons (HCs), which are also sources for syngas. Hence, catalytic steam reforming is an effective technique to address tar formation and improve H₂ production from biomass gasification. Of the various classes in existence, supported metal catalysts are considered the most promising. This paper focuses on the current researching status, prospects, and challenges of steam reforming of gasified biomass tar. Besides, it includes recent developments in tar compositional analysis, supported metal catalysts, along with the reactions and process conditions for catalytic steam reforming. Moreover, it discusses alternatives such as dry and autothermal reforming of tar.